Similar to other grades of aluminum bronze, C95500 contains nickel. Nickel makes C95500 aluminum bronze one of the toughest non-ferrous alloys known. The alloy exhibits exceptional yield, compressive strength, high hardness, and fairly high elongation. It is an excellent bearing material suitable for heavy duty, high shock, and high impact applications. The alloy has good resistance to sea water corrosion, heat resistance, good machinability, and weldability.
Also known as: CDA 955, ASTM B-148 Alloy 9D, ASTM B-271 Alloy C95500, ASTM B-584 Alloy C95500, ASTM B-505 Alloy C95500, ASTM B-763, SAE J461, J462, QQC-390 Alloy G3, QQC-390 Rev. A/B Alloy C95500, Mil B-16033-4, Mil C-15345-14, WCI-230, CuAl10Ni, CC333G, AB2, Ingot 415, Aluminum Bronze 9D, 81-4-4-11.
| Cu% | Sn% | Pb% | Zn% | Fe% | Ni% | Sb% | P% | S% | AI% | Mn% | Si% |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 78.00 MIN | N/A | N/A | N/A | 3.00- 5.00 |
3.00- 5.50 |
N/A | N/A | N/A | 10.00- 11.50 |
3.50 | N/A |
Typical Uses
- Builders Hardware:
- Window Hardware
- Consumer:
- Musical Instruments, Piano Keys
- Electrical:
- Electrical Hardware
- Fasteners:
- Stuffing Box Nuts
- Industrial:
- Machine Parts, Glass Molds, Welding Jaws, Wear Plates, Air Craft Components, Pickling Equipment, Valve Guides, Piston Guides, Valve Seats, Pump Fluid Ends, Worms, Worm Wheels, Hot Mill Guides, Landing Gear Parts, Sewage Treatment Applications, Valve Components, Bearings, Gears, Bushings, Valve Bodies, Landing Gear Parts, Hand Gun Recoil Mechanisms
- Marine:
- Ship Building, Covers for Marine Hardware, Marine Applications, Marine Hardware
- Ordnance:
- Government Fittings
Nickel Aluminum Bronze Properties
| Mechanical - Nickel Aluminum Bronze | ||
|---|---|---|
| Tensile Strength, min | 95 ksi | 655 MPa |
| Yield Strength @ .5% ext under load min | 42 ksi | 290 MPa |
| Elongation in 2 in. or 50 mm min, % | 10 | |
| Brinell Hardness, min | N/A | |
| Machinability Rating | 50% | |
| Physical - Nickel Aluminum Bronze | ||
|---|---|---|
| US Customary | Metric | |
| Melting Point-Liquidus | 1930 F | 1054 C |
| Melting Point-Solidus | 1900 F | 1038 C |
| Density | 0.272 lb/in3 @ 68 F | 7.53 gm/cm3 @ 20 C |
| Specific Gravity | 7.530 | 7.53 |
| Electrical Resistivity | 122.80 ohms-cmil/ft @ 68 F |
20.41 microhm-cm @ 20 C |
| Electrical Conductivity | 80 %IACS @ 68 F | 0.049 MegaSiemens/cm @ 20 C |
| Thermal Conductivity | 24.20 Btu ft/ (hr ft2 oF) @ 68 F |
41.9 W/m oK @ 20 C |
| Coefficient of Thermal Expansion |
90 10-6 per oF (68-572 F) |
16.2 10-6 per oC (20-300 C) |
| Specific Heat Capacity | 0.10 Btu/lb/oF @ 68 F |
419.0 J/kg oK @ 293 K |
| Modulus of Elasticity in Tension |
16000 ksi | 110000 MPa |
| Magnetic Permeability* | 1.320 | 1.32 |
| *Field Strength 16 kA/m | ||
| Fabrication - Nickel Aluminum Bronze | |
|---|---|
| Joining Technique | Suitability |
| Soldering | Good |
| Brazing | Fair |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |